Pengaruh Konsentrasi dan Waktu Aktivasi Katalis Palladium pada Electroless Plating Nickel Permukaan Plastik ABS

Muhammad Budi Nur Rahman, Sunardi Sunardi, Auliandi Luthfi Wibisono, Bayu Anggara

Abstract


ABS plastic is widely used for automotive components and interior design because of its lightweight, easily shaped, strong, but low hardness, no friction-resistant, and heat resistant. Electro less plating is a method of metallization before electro plating to improve the quality and appearance. To get a good bond between plastic and metal is necessary to the activation of the palladium which is influence by concentration, temperature and activation time. The research aims to determine the influence of the palladium solution concentration and activation time of the electroless nickel plating process on surface roughness, layer thickness, hardness and wear resistance of ABS plastic. The concentration of palladium was prepared at 3%, 5% and 7% in HCl solution (37%). The activation time was carried out during 4 to 12 minutes. The research shows that those parameters increase wear resistance of the surface. In addition the activation time parameter is also found to increase layer thickness and roughness value of the specimens. Yet, those parameters are not found to affect significantly on its hardness value.


Keywords


electroless plating nickel, ABS plastic, palladium concentration, activation time

Full Text:

PDF

References


Equbal, A., and Sood. K.A. Metallization on FDM Parts Using the Chemical Deposition Technique. Coatings, 2014; 4 (3): 574-586.

Mujiarto, I. Sifat dan karakteristik material plastik dan bahan aditif. Traksi, 2005; 3(2): 65.

Santhiarsa, N. Pengaruh Temperatur Larutan dan Waktu Pelapisan Elektroles Terhadap Ketebalan Lapisan Metal Dipermukaan Plastik ABS. Prosiding Konferensi Nasional Engineering Perhotelan, 2016; VII 4 (1): 22.

Shao, Z., Z. Cai, R. Hu, and S. Wei., The study of electroless nickel plating directly on magnesium alloy. Surface & Coating Technology, 2014; 249: 42-47.

Tang, X., M. Cao, C. Bi, L. Yan, and B. ZhangResearch on a New Surface Activation Process for Electroless Plating. Materials Letters . 2007; 62: 1089-1091.

Gui-Xiang., W., Li. N., Li. D., “Effect of Palladium ions in the chemical etching solution.” Journal of University of Science and Technology Beijing Mineral Metallurgy Material, 2007; 14(3):286-289

Olivera, S., H. B. Muralidhara, K. Venkatesh, K. Gopalakrishna, and C. S. Vivek., Plating on acrylonitrile–butadiene–styrene (ABS) plastic. Springer Science 2016: 51 (8): 3657–3674.

Yulianto, S. R., and E. Widodo, “Analisa Pengaruh Variasi Temperatur Proses Pelapisan Nikel Khrom Terhadap Kualitas Ketebalan Dan Kekerasan Pada Baja ST 40.” SNFT UMSIDA, 2013;145-149.

Domenech, S.C., E. Lima Jr, V. Drago, J.C. De Lima, N.G. Borges Jr, A.O.V Avila, and V. Soldi. Electroless Plating of Nickel–Phosphorous on Surface-Modified Polyethylene terephthalate Films.” Applied Surface Science 220. 2003; 1-4: 238–250.

Krulik, G. A. “Tin-Palladium Catalysts for Electroless Plating. Platinum Metals Review 6. 1982; 2: 58-64.

Wang, G. X., N. Li, H. L. Hu, and Y. C. Yu. Process of Direct Copper Plating on ABS Plastics. Applied Surface Science 253. 2006; 2: 480-484.




DOI: https://doi.org/10.18196/jmpm.2122

Refbacks

  • There are currently no refbacks.


Editorial Office :

JURNAL MATERIAL DAN PROSES MANUFAKTUR

Department of Mechanical of Engineering, Faculty of Engineering, Universitas Muhammadiyah Yogyakarta.

Jln. Brawijaya Tamantirto Kasihan Bantul 55183 Indonesia

Telp:(62)274-387656, Fax.:(62)274-387656, WA: 085729357100

Email: jmpm@umy.ac.id

Website: http://http://journal.umy.ac.id/index.php/jmpm