Analisa Pengaruh Preheating dan Post Weld Quench terhadap Kekuatan dan Struktur Mikro Baja S45C dengan Pengelasan Shielded Metal Arc Welding

Authors

  • Arif Rachman Departemen Teknik Mesin, Fakultas Teknik, Universitas Singa Perbangsa, Indonesia
  • Iman Dirja Departemen Teknik Mesin, Fakultas Teknik, Universitas Singa Perbangsa, Indonesia
  • Reza Setiawan Departemen Teknik Mesin, Fakultas Teknik, Universitas Singa Perbangsa, Indonesia

DOI:

https://doi.org/10.18196/jqt.v6i2.23046

Keywords:

SMAW, S45C Material

Abstract

In many industrial contexts, steel is an everyday material. The technique of attaching metal parts using heat energy, known as welding, is something we encounter often; S45C is one of several steels that are used in machine construction. Protected metal arc welding is one type of welding that we come across frequently. Unwanted metallurgical changes, deformation, or residual stress in the base metal might occur as a consequence of uneven or excessive heating. A better method is to heat it up beforehand, often known as preheating, before welding. Determining the effect of preheating on the hardness of S45C steel during welding is one of the primary aims of this study. (2) to understand how changes in temperature and time affect the microstructure of S45C steel during welding and how it affects the final product. (3) ascertain the effect of temperature and duration on the resulting hardness of S45C steel welding. During the preheating procedure, the temperature is varied between 160 and 260 degrees Celsius, and the waiting periods are 7, 15, and 20 minutes, respectively. Hardness and microstructure testing, also known as metalografy, is performed on S45C steel after shielded metal arc welding (SMAW) to ascertain the degree of hardness and microstructure of the steel.

References

Eka Setyawan, P., Surya Irawan, Y., & Suprapto, W. (2014). Kekuatan Tarik dan Porositas Hasil Sambungan Las Gesek Aluminium 6061 dengan Berbagai Suhu Aging. Jurnal Rekayasa Mesin, 5(2), 141–148.

Faruq, A., & Rasyid, A. (2020). Pengaruh Sudut Chamfer Male – Female Dan Tekanan Gesek Pada Proses Friction Welding Baja Karbon S45c Terhadap Kekuatan Tarik Dan Struktur Mikro. Jurnal Pendidikan Teknik Mesin Unesa, 1(1), 0–216.

Fatkhurrohman, F., Ismail, I., & Yudhanto, F. (2022). Analisis Kekuatan Bending Komposit Lamina Serat Ijuk Anyam dan Serat Ijuk Acak bermatriks Polyester. Quantum Teknika : Jurnal Teknik Mesin Terapan, 4(1), 55–61. https://doi.org/10.18196/jqt.v4i1.16593

Hakim, Lukman et al., 2018. (2018). Pengaruh Variasi Tekanan Gesek Terhadap Kekuatan Tarik Struktur Mikro Dan Kekerasan Sambungan Las Metode Continuous Drive Friction Welding Bahan Silinder Pejal Logam Stainless Steel 304. 1–10.

Husodo, N., Sanyoto, B. L., Setyawati, S. B., & Mursid, M. (2013). Penerapan Teknologi Las Gesek (Friction Welding) dalam Rangka Penyambungan Dua Buah Logam Baja Karbon St41 pada Produk Back Spring Pin. Jurnal Energi Dan Manufaktur, 6(1), 43–52.

Kasijanto, K., Wahjudi, S., & Listiono, L. (2018). Pengaruh Konfigurasi Sudut Chamfer Male-Female dan Lama Gesek Terhadap Karakteristik Hasil Pengelasan dan Kekuatan Tarik Paduan Alumunium 6061. Jurnal Energi Dan Teknologi Manufaktur (JETM), 1(02), 01–08. https://doi.org/10.33795/jetm.v1i02.18

Kido, M. I., Sugiarto, S., & Darmadi, D. B. (2021). Perubahan Sifat Mekanik Hasil Pengelasan Gesek Aluminium 6061 Akibat Perubahan Temperatur Lingkungan. Jurnal Rekayasa Mesin, 12(1), 95. https://doi.org/10.21776/ub.jrm.2021.012.01.11

Ridono, T. W., Zaenudin, M., & Gamayel, A. (2024). Simulasi Dan Analisis Desain Mold Dengan Software Autodesk Fusion 360 Untuk Produk Aksesoris. Quantum Teknika : Jurnal Teknik Mesin Terapan, 25(1), 11–20.

Solihin, Sukmana, I., & Ummah, K. (2018). Pengaruh waktu kontak terhadap kualitas sambungan hasil las gesek (Friction Welding) Magnesium AZ-31. Jurnal Energi Dan Manufaktur, 10(1), 4–7.

Sugianto, H. (2016). Pengaruh Waktu Gesek Dan Sudut Chamfer Terhadap Sifat Mekanik Hasil Lasan Aluminium 6061 Pada Proses Friction Welding. 1–61.

Tsamroh, D. I., & Riza Fauzy, M. (2022). Peningkatan Sifat Mekanik Al6061 Melalui Heat Treatment Natural-Artificial Aging. G-Tech: Jurnal Teknologi Terapan, 6(1), 8–13. https://doi.org/10.33379/gtech.v6i1.1217

Downloads

Published

2025-04-30

How to Cite

Rachman, A., Dirja, I., & Setiawan, R. (2025). Analisa Pengaruh Preheating dan Post Weld Quench terhadap Kekuatan dan Struktur Mikro Baja S45C dengan Pengelasan Shielded Metal Arc Welding. Quantum Teknika : Jurnal Teknik Mesin Terapan, 6(2), 78–81. https://doi.org/10.18196/jqt.v6i2.23046

Issue

Section

Articles