Pengaruh Penambahan Serat Limbah Plastik HDPE terhadap Kuat Tekan pada Mortar
Abstract
Mortar is a construction material commonly used in building and road infrastructure. Some constructions that use mortar include Lane Concrete (LC), species, light brick adhesives, wall plaster, mechanical installation, and others. HDPE plastic waste fiber (High density polyethylene) in this study is a mixture of materials as binders and cement substitutes. HDPE plastic is one type of plastic that when viewed visually is classified as concentrated, where the use of this type of plastic is usually used for beverage bottles. The HDPE plastic type is easy to recycle. In 2015, global plastic waste in the world was recorded at 2.5 billion tons per year, so this research is expected to reduce the amount of plastic waste in Indonesia. The purpose of this study was to analyze the effect of mixing HDPE plastic waste fibers on compressive strength and mortar weight. This HDPE variations of 0%, 2%, 4%, and 6% is used from the weight of the cement. This study was carried out to obtain the compressive strength at the ages of 7 days and 28 days using cube specimens with dimensions of 15 cm × 15 cm × 15 cm. Based on the results of the test, the highest compressive strength for mortar at of 2% fiber variation at 28 days is 14.47 MPa. The compressive strength of mortar at the age of 7 and 28 consecutive days increased by 11%. While the addition of fibers, compressive strength of mortar decreases with the increasing number of fiber mixtures. Fiber mortar decreased in weight from 7696 grams to 7640 grams, 7422 grams, and 7280 grams, for fiber of 2%, 4%, and 6% respectively.
Keywords
Full Text:
PDFReferences
Lomboan, F. O., Kumaat, E. J., & Windah, R. S. (2016). Pengujian Kuat Tekan Mortar Dan Beton Ringan Dengan Menggunakan Agregat Ringan Batu Apung Dan Abu Sekam Padi Sebagai Substitusi Parsial Semen. Jurnal Sipil Statik, 4(4).
Maskur, I., Satyarno, I., & Siswanto, M. (2017). Perancangan Campuran Flow Mortar Untuk Pembuatan Self-Compacting Concrete Dengan FAS 0,5. Dinamika Rekayasa, 13(2), 89-96.
Qomariah. (2015). Pengaruh Penambahan Cacahan Botol Aqua Polypropylene (PP) pada Pasir terhadap Kinerja Beton Normal. Prokons: Jurnal Teknik Sipil, 11(1), 21-26.
Simanullang, D. Y. (2014). Kajian Kuat Tekan Mortar Menggunakan Pasir Sungai dan Pasir Apung dengan Bahan Tambah Fly Ash dan Conplast dengan Perawatan (Curing). Journal of Civil and Environmental Engineering, 2(4).
Soebandono, B., Pujianto, A., & Kurniawan, D. (2013). Perilaku Kuat Tekan dan Kuat Tarik Beton Campuran Limbah Plastik HDPE. Semesta Teknika, 16(1).
DOI: https://doi.org/10.18196/bce.v1i2.12418
Refbacks
- There are currently no refbacks.
Editorial Office :
BULLETIN OF CIVIL ENGINEERING
Universitas Muhammadiyah Yogyakarta.
Jln. Brawijaya Tamantirto Kasihan Bantul 55183 Indonesia
Telp:(62)274-387656, Fax.:(62)274-387656
Website: http://journal.umy.ac.id/index.php/bce
Print ISSN : 2797-1104
Online ISSN : 2775-6351
Bulletin of Civil Engineering is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.