Analisis Pengaruh Parameter Hardening terhadap Distorsi Spesimen CT58 dengan Metode Taguchi

Article Sidebar

PDF
Published: Dec 12, 2023
DOI: https://doi.org/10.18196/jmpm.v7i2.20073

Main Article Content

Perwita Kurniawan
Politeknik ATMI Surakarta
Millenino Bergas Sartoyo
Politeknik ATMI Surakarta
Aditya Nugraha
Politeknik ATMI Surakarta
Adi Nugroho
Politeknik ATMI Surakarta

Abstract

Penelitian ini membahas masalah distorsi komponen mesin rokok setelah proses hardening. Penelitian ini berfokus pada perubahan dimensi diameter dalam lubang, lebar gap, dan kerataan pada komponen. Temperatur austenit, media quench, dan  temperatur tempering diperiksa untuk menentukan pengaruhnya terhadap distorsi. Komponen terbuat dari kelompok baja mesin S45C setara AISI 1045. Penelitian ini menggunakan spesimen bernama CT58 dengan variasi temperature Austenite 820˚C 840˚C 860˚C, lalu variasi media quenching oli, oli+air, dan air dan variasi temperature Tempering 200˚C, 250˚C, dan 300˚C. Penelitian ini menggunakan Design of Experiment, dilanjutkan dengan analisis statistik dengan aplikasi minitab. Hasil penelitian didapatkan bahwa distorsi pada spesimen CT58 paling besar dipengaruhi oleh suhu Austenite dan diikuti oleh media Quench dan suhu Tempering. Temperatur austenit 820°C, media quench oli, dan temperatur tempering 250°C merupakan parameter pengerasan terbaik untuk aspek Inner Diameter. Temperatur austenit 820°C, media quench oli, dan temperatur tempering 250°C merupakan parameter pengerasan terbaik untuk aspek Gap Width. Temperatur austenit 820°C, media quench oli, dan temperatur tempering 250°C merupakan parameter pengerasan terbaik untuk aspek Flatness.

Article Details

How to Cite
Kurniawan, P., Sartoyo, M. B., Nugraha, A., & Nugroho, A. (2023). Analisis Pengaruh Parameter Hardening terhadap Distorsi Spesimen CT58 dengan Metode Taguchi. JMPM (Jurnal Material Dan Proses Manufaktur), 7(2), 152–159. https://doi.org/10.18196/jmpm.v7i2.20073
Issue
Vol. 7 No. 2 (2023): Desember
Section
Articles

License

Creative Commons License


JMPM (Jurnal Material dan Proses Manufaktur) is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License. You are free to :

  1. Adapt — remix, transform, and build upon the material for any purpose, even commercially.

The licensor cannot revoke these freedoms as long as you follow the license terms, which include the following:

  • Attribution — You must give appropriate credit, provide a link to the license, and indicate if changes were made. You may do so in any reasonable manner, but not in any way that suggests the licensor endorses you or your use.

  • ShareAlike — If you remix, transform, or build upon the material, you must distribute your contributions under the same license as the original.

References

Alfian Siswara Arlingga, Somawardi, & Sugianto. (2021). Analisis Pengaruh Media Pendingin Terhadap Kekerasan Baja S45C Pada Proses Hardening-Tempering. SJoME, 3(1).

Fauzi Rachman, F., & Rumendi, U. (2014). Analisis Pengaruh Variasi Temperatur Media Quenching Pada Proses Hardening Terhadap Kekerasan Permukaan Dan Tingkat Distorsi Baja AISI 1045. Steman.

Handoyo, Y. (2015). Pengaruh Quenching Dan Tempering Pada Baja Jis Grade S45C Terhadap Sifat Mekanis. In Jurnal Imiah Teknik Mesin (Vol. 3, Issue 2). http://ejournal.unismabekasi.ac.id/

Pramono, A. (2011b). Karakterisrik Mekanik Proses Hardening Baja Aisi 1045 Media Quenching Untuk Aplikasi Sprochet Rantai. In Jurnal Ilmiah Teknik Mesin (Vol. 5, Issue 1). www.uddeholm.com

Susri Mizhar dan Suherman. (2011). PENGARUH PERBEDAAN KONDISI TEMPERING TERHADAP STRUKTUR MIKRO DAN KEKERASAN DARI BAJA AISI 4140. Jurnal Dinamis, II(8).