Analisis Kekerasan Hasil Pengelasan Gas Tungsten Arc Welding pada Baja ST 37 dengan Variasi Media Pendingin

Gede Agus Widiantara, I Nyoman Pasek Nugraha, Kadek Rihendra Dantes

Abstract


Cooling media is a substance that increases the hardness value of a material through a heat-treatment process. This study aims to determine the effect of cooling media on the hardness of ST 37 steel due to Gas Tungsten Arc Welding (GTAW). The independent variables, namely water cooling media, seawater cooling media, and oil cooling media, while the dependent variable is the hardness. The specimens using water cooling media, the hardness in the weld area is 47.19 kg/mm2, in the HAZ area the it is 54.6 kg/mm2, and the base metal gets a value of 40.87 kg/mm2. While the specimens with seawater cooling media get a value in the weld area of 76.37 kg/mm2, in the HAZ area it gets a value of 83.89 kg/mm2 and the base metal gets a value of 70.13 kg/mm2. The specimens with oil cooling media the value in the weld area is 40.77 kg/mm2, in the HAZ area it gets a value of 43.32 kg/mm2 and the base metal gets a value of 36.09 kg/mm2 . From the hardness values obtained, specimens immersed in seawater cooling media have the higher hardness values compared than water and oil cooling media.


Keywords


Cooling Media; Hardness; ST 37.

Full Text:

PDF

References


Purwohandoyo, D. A. 2018. Pengaruh Variasi Media Pendingin (Air Laut, Air Sumur dan Oli Sae 40) terhadap Sifat Fisis Dan Kekerasan Hasil Pengecoran Kuningan (CuZn) Menggunakan Cetakan Pasir CO2. (Diploma thesis, Universitas Muhammadiyah Surakarta).

Darma, K. B. S., Widayana, G., & Nugraha, I. N. P. 2017. Pengaruh Media Pendinginan Terhadap Sifat Mekanik Hasil Pengelasan Material ST 37. Jurnal Pendidikan Teknik Mesin Undiksha, 5(1).

Imawan, D. 2017. Pengaruh Variasi Pendinginan pada Proses Quenching terhadap Nilai Kekerasan, Struktur Mikro dan Ketangguhan Hasil Pengecoran Aluminium Limbah Piston. (Skripsi, Universitas Negeri Semarang).

Kolo, J. M., Nugraha, I. N. P., & Widayana, G. 2017. Pengaruh Variasi Arus terhadap Kekuatan Impact dan Kekerasan Material ST 37 Menggunakan Proses Pengelasn Gas Tungsten Arc Welding (GTAW). Jurnal Pendidikan Teknik Mesin Undiksha, 5(2).

Nurisna, Z., & Setiawan, E. 2020. Pengaruh Filler Pada Pengelasan Tig Baja Karbon dan Stainless Steel 316L terhadap Sifat Mekanik. Quantum Teknika: Jurnal Teknik Mesin Terapan, 1(2), 95-99.




DOI: https://doi.org/10.18196/jqt.v3i1.12245

Refbacks

  • There are currently no refbacks.


Copyright (c) 2021 Quantum Teknika : Jurnal Teknik Mesin Terapan



Quantum Teknika : Jurnal Teknik Mesin Terapan is indexed by :

 

Office:

Editorial of Quantum Teknika, Building D, Jl. Brawijaya, Tamantirto, Kasihan, Bantul, Yogyakarta.

Telp: (0274) 387656
Fax: (0274) 387646
WA: +62896-7470-8638 (Mirza Yusuf)
Email: jqt@umy.ac.id

Creative Commons License
Quantum Teknika : Jurnal Teknik Mesin Terapan is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.